產(chǎn)品詳情
一、S355G9+N、S355G9+M執(zhí)行技術(shù)標(biāo)準(zhǔn)：EN 10225-2009
二、S355G9+N鋼板化學(xué)成分
|
牌號 |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Cu |
|
S355G9+N |
≤0.12 |
0.15~0.55 |
≤1.65 |
≤0.02 |
≤0.010 |
≤0.7 |
≤0.2 |
≤0.08 |
≤0.3 |
|
Nb |
V |
Ti |
Alt |
N |
B |
Ca |
Pb |
CeqMax |
PcmMax |
|
≤0.03 |
≤0.06 |
≤0.025 |
0.015~0.055 |
≤0.010 |
≤0.0005 |
≤0.005 |
≤0.010 |
≤0.43 |
≤0.22 |
三、S355G9+M鋼板化學(xué)成分成品分析
|
牌號 |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
|
S355G9+M |
≤0.12 |
0.15~0.55 |
≤1.65 |
≤0.02 |
≤0.010 |
≤0.7 |
≤0.2 |
≤0.08 |
|
Cu |
Nb |
V |
Ti |
Alt |
N |
B |
Ca |
Pb |
|
≤0.3 |
≤0.03 |
≤0.06 |
≤0.025 |
0.015~0.055 |
≤0.010 |
≤0.0005 |
≤0.005 |
≤0.010 |
成分備注：As、Sn、Pb、Bi、Ca、B為殘余元素；Nb+V≤0.06；Nb+V+Ti≤0.08；Alt/N≥2；As≤0.03；Sn≤0.02；Bi≤0.01；厚度＞75mm，交貨條件為熱機(jī)械軋制時(shí)，Mo≤0.2；厚度＞40mm，Ni≥0.3。Ceq = C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15 Pcm=C+Si/30+(Mn+Cu+Cr)/20+Ni/60+Mo/15+V/10+5B
四、S355G9+N鋼板力學(xué)性能
|
牌號 |
抗拉強(qiáng)度MPa |
對應(yīng)厚度（mm）的下屈服強(qiáng)度MPa |
伸長率A% |
沖擊功 |
|||||||
|
厚度≤100mm |
厚度＞100mm |
≤16 |
16-25 |
25-40 |
40-63 |
63-100 |
100-150 |
溫度℃ |
能量J |
||
|
S355G9+N |
470-630 |
460-620 |
355 |
355 |
345 |
335 |
325 |
320 |
22 |
-40 |
50 |
五、S355G9+M鋼板力學(xué)性能
|
牌號 |
抗拉強(qiáng)度MPa |
對應(yīng)厚度（mm）的下屈服強(qiáng)度MPa |
伸長率A% |
沖擊功 |
|||||
|
厚度≤100mm |
≤16 |
16-25 |
25-40 |
40-63 |
63-100 |
溫度℃ |
能量J |
||
|
S355G9+M |
470-630 |
355 |
355 |
345 |
335 |
325 |
22 |
-40 |
50 |
六、S355G9+N與S355G9+M簡介及應(yīng)用
S355G9+N、S355G9+M是固定海上構(gòu)架用焊接結(jié)構(gòu)鋼，屬于海洋平臺結(jié)構(gòu)鋼， “S”表示為結(jié)構(gòu)鋼，“355”表示為鋼板更低屈服強(qiáng)度，G9表示鋼種特性的相關(guān)數(shù)字，N是正火或正火軋制交貨狀態(tài)，M是熱機(jī)械軋制（TMCP）狀態(tài)交貨。具有**的機(jī)械性能、焊接性能、工藝性能，適用于制造遠(yuǎn)洋、近海的采油平臺、碼頭設(shè)備等結(jié)構(gòu)件。S355G9+N、S355G9+M舞陽鋼廠可以生產(chǎn)，訂軋，交期快價(jià)格優(yōu)。