| 品名 | 鐵基合金粉 | 產(chǎn)地 | 上海 | 鐵含量≥ | 1-99（%） |
| 粒度 | 120-320（目） | 牌號(hào) | 鐵粉 | 形狀 | 顆粒狀 |
| 制作方法 | 霧化法 | 包裝規(guī)格 | 桶 |
噴涂合金粉末 Sprayed alloy powder
凡金屬合金粉末都可以用于等離子噴涂，氧乙炔火焰噴涂以及超音速噴涂，以下介紹是我公司生產(chǎn)的常用的典型噴涂粉末，建議用戶在使用前必須在爐內(nèi)加熱到120℃保溫兩小時(shí)后，隨爐冷至常溫即可使用。
All of the bl alloy powders can be used for plasma Spraying, oxyacetylene flame spraying and supersonic Spraying, The following typical sprayed coating powder should be heated in the stove until 120℃. Then, the heat of the power should be preserved for two hours and later be cooled to the normal temperature before useing.
All of the bl alloy powders can be used for plasma Spraying, oxyacetylene flame spraying and supersonic Spraying, The following typical sprayed coating powder should be heated in the stove until 120℃. Then, the heat of the power should be preserved for two hours and later be cooled to the normal temperature before useing.
| 型號(hào) | 規(guī)格(μm) | 特性用途 | 物理性能 | 應(yīng)用工藝 |
| NiCr |
-106/+45 -45/+15 |
抗高溫氧化溫度達(dá)800℃左右，是高溫耐磨涂層，也是金屬陶瓷粉工作層的底層粘結(jié)粉。 |
①Rb80 ②熔點(diǎn)1400℃ ③流動(dòng)性20s/50g ④松裝密度4.6g/cm3 |
氧乙炔 等離子 超音速 |
| NiCrAl |
-106/+45 -45/+15 |
具有良好的抗高溫氧化、耐燃?xì)馇治g性能使用溫度可達(dá)1000℃有較高穩(wěn)定性，也可用于高溫的AL2O3陶瓷涂層的粘結(jié)底層?！? |
①Rb58-62 |
同上 |
| NiCrMo |
-106/+45 -45/+15 |
該合金為哈氏特合金系列，具有極優(yōu)抗氯離子腐蝕能力。 |
①Rb60-70 ②熔點(diǎn)1400℃ ③流動(dòng)性20s/50g ④松裝密度4.6g/cm3 |
同上 |
| NiCrFe |
-106/+45 -45/+15 |
這是一些種耐熱，耐腐蝕性能優(yōu)良的合金，在1000℃以下具有良好的抗氧化性，在硫酸、硝酸、醋酸、乳酸、氨、氫氧化物中耐腐蝕性良好，如鋁的澆鑄模，熔化和澆鑄坩堝等。 |
①Rb60 |
同上 |
| Ni-Cu |
-106/+45 -45/+15 |
該合金為蒙乃爾合金系列具有優(yōu)良的耐腐蝕性，特別對(duì)氫氟酸的耐腐蝕性非常好和在海洋環(huán)境的各種泵的柱塞，旋轉(zhuǎn)軸，密封環(huán)以及氫氟酸環(huán)境用軸類等。 |
①Rb50 ②熔點(diǎn)1320℃ ③流動(dòng)性17s/50g ④松裝密度4.8g/cm3 |
同上 |
|
316 316L 304 304L 410 420 |
-106/+45 -45/+15 |
該類合金粉均用于不同防腐和耐磨涂層。 | 同上 |