產(chǎn)品詳情
| 規(guī)格 ( mm ) | 精度等級 ( μm ) | |||
| 0 | 1 | 2 | 3 | |
| 100 × 100 | 4 | 8 | 16 | |
| 200 × 100 | 5 | 10 | 20 | |
| 200 × 200 | 5 | 10 | 20 | |
| 300 × 200 | 6 | 12 | 24 | |
| 300 × 300 | 6 | 12 | 24 | |
| 400 × 300 | 6 | 12 | 24 | |
| 400 × 400 | 6 | 12 | 24 | |
| 500 × 400 | 6 | 12 | 24 | |
| 600 × 400 | 7 | 14 | 28 | |
| 600 × 500 | 7 | 14 | 28 | |
| 800 × 400 | 8 | 16 | 32 | 80 |
| 800 × 600 | 8 | 16 | 32 | 80 |
| 900 × 600 | 8 | 16 | 32 | 80 |
| 1000 × 750 | 18 | 36 | 90 | |
| 1000 × 1000 | 20 | 39 | 96 | |
| 1200 × 1000 | 20 | 39 | 96 | |
| 1500 × 1000 | 24 | 48 | 120 | |
| 2000 × 1000 | 26 | 52 | 129 | |
| 2000 × 1500 | 56 | 140 | ||
| 2000 × 2000 | 60 | 152 | 230 | |
| 3000 × 1000 | 168 | 248 | ||
| 3000 × 1500 | 174 | 254 | ||
| 3000 × 2000 | 184 | 275 | ||
| 4000 × 2000 | 219 | 310 | ||
| 4000 × 3000 | 240 | 360 | ||
| 6000 × 3000 | 308 | 460 | ||
鑄鐵平板按GB/4986-85標(biāo)準制造，產(chǎn)品制成筋板式和箱體式，工作面有長方形，材料HT200,工作面采用刮研工藝，工作面上可加工V型、T型、U型槽和圓孔、長孔等。鑄鐵平板是用于工件檢測或劃線的平面基準器具。鑄鐵平板安裝應(yīng)調(diào)至水平、負荷均分布于各支點上，環(huán)境溫度使用時應(yīng)避免振動。
鑄鐵平板特點：
鑄鐵平板使用磨損后，可以重新修刮恢復(fù)其精度。
鑄鐵平板可用涂色法檢驗零件平面度，具有準確、直觀、方便的優(yōu)點。在經(jīng)過刮研的鑄鐵平板上推動表座、工件比較順暢，無發(fā)澀感覺，方便了測量，保證了測量準確度。
鑄鐵平板的鑄鐵質(zhì)量和熱處理質(zhì)量對平板使用性能產(chǎn)生較大影響：或因殘存較大內(nèi)應(yīng)力使工作面變形；或因不耐磨損使精度不能保持；或因刮削困難得不到數(shù)值小的粗糙度。因此使用鑄鐵平板必須注意鑄鐵材料的選擇，采用時效處理等方法消除鑄鐵平板的殘余應(yīng)力
鑄鐵平板特點：
鑄鐵平板使用磨損后，可以重新修刮恢復(fù)其精度。
鑄鐵平板可用涂色法檢驗零件平面度，具有準確、直觀、方便的優(yōu)點。在經(jīng)過刮研的鑄鐵平板上推動表座、工件比較順暢，無發(fā)澀感覺，方便了測量，保證了測量準確度。
鑄鐵平板的鑄鐵質(zhì)量和熱處理質(zhì)量對平板使用性能產(chǎn)生較大影響：或因殘存較大內(nèi)應(yīng)力使工作面變形；或因不耐磨損使精度不能保持；或因刮削困難得不到數(shù)值小的粗糙度。因此使用鑄鐵平板必須注意鑄鐵材料的選擇，采用時效處理等方法消除鑄鐵平板的殘余應(yīng)力