PA66 A3Z HP UV 自潤性、聚酰胺俗稱尼龍（Nylon），英文名稱Polyamide（簡稱PA），是分子主鏈上含有重復(fù)酰胺基團(tuán)—[NHCO]—的熱塑性樹脂總稱。包括脂肪族PA，脂肪—芳香族PA和芳香族PA。其中，脂肪族PA品種多，產(chǎn)量大，應(yīng)用廣泛，其命名由合成單體具體的碳原子數(shù)而定。
| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Mechanical Properties | Maetric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D786 |
| Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
尼龍是最重要的工程塑料，產(chǎn)量在五大通用工程塑料中居首位。 尼龍,是聚酰胺纖維（錦綸）是一種說法. 可制成長纖或短纖。, 工程塑料:玻璃纖維增強(qiáng)尼龍66(PA66+GF30)