產(chǎn)品詳情
項(xiàng)目
測(cè)試條件
屬性值
單位
測(cè)試方法
物理性能 |
||||
| 熔指(MFR) | 載荷 5.0kg,temperature 280℃ |
|
g/10 min | ASTM D1238 |
| 吸濕性 |
|
% | ASTM D570 | |
| 密度 |
|
無(wú) | ASTM D792 | |
| 收縮率 | 橫向 |
|
cm/cm | SABIC Method |
| 收縮率 | 流動(dòng)，thickness 3.2mm |
|
cm/cm | SABIC Method |
機(jī)械性能 |
||||
| 拉伸屈服強(qiáng)度 | type I，50mm/min |
|
MPa | ASTM D638 |
| 洛氏硬度 | R級(jí) |
|
無(wú) | ASTM D785 |
| 拉伸模量 | 5mm/min |
|
GPa | ASTM D638 |
| 拉伸模量 | 1mm/min |
|
GPa | ISO 527 |
| 彎曲模量 |
|
GPa | ISO 178 | |
| 彎曲模量 | 2.6mm/min,100mm span |
|
GPa | ASTM D790 |
| 彎曲模量 | 1.3mm/min,50mm span |
|
GPa | ASTM D790 |
| 落錘沖擊 | temperature 23℃ |
|
J | ASTM D3763 |
| 屈服伸長(zhǎng)率 | type I，50mm/min |
|
% | ASTM D638 |
| 屈服伸長(zhǎng)率 |
|
% | ISO 527 | |
| 拉伸斷裂強(qiáng)度 | type I，50mm/min |
|
MPa | ASTM D638 |
| 拉伸斷裂強(qiáng)度 |
|
MPa | ISO 527 | |
| 拉伸斷裂強(qiáng)度 |
|
MPa | ISO 527 | |
| 懸臂梁缺口沖擊強(qiáng)度 | temperature -300℃ |
|
J/cm | ASTM D256 |
| 懸臂梁缺口沖擊強(qiáng)度 | 80*10*4 |
|
kJ/m2 | ISO 180/1A |
| 懸臂梁缺口沖擊強(qiáng)度 |
|
J/cm | ASTM D256 | |
| 斷裂伸長(zhǎng)率 | type I，50mm/min |
|
% | ASTM D638 |
| 斷裂伸長(zhǎng)率 |
|
% | ISO 527 | |
| 彎曲強(qiáng)度 | 1.3mm/min,50mm span |
|
MPa | ASTM D790 |
| 彎曲強(qiáng)度 |
|
MPa | ISO 178 | |
| 彎曲強(qiáng)度 | 2.6mm/min,100mm span |
|
MPa | ASTM D790 |
熱性能 |
||||
| 載荷下熱變形溫度 | 1.8mpa |
|
°C | ISO 75/Ae |
| 載荷下熱變形溫度 | 0.46mpa |
|
°C | ISO 75/Be |
| 載荷下熱變形溫度 | 1.8mpa,thickness 6.4mm |
|
°C | ASTM D648 |
| 載荷下熱變形溫度 | 1.8mpa,thickness 3.2mm |
|
°C | ASTM D648 |
| 載荷下熱變形溫度 | 0.46mpa |
|
°C | ASTM D648 |
| 維卡軟化點(diǎn) |
|
°C | ISO 306 | |
| 維卡軟化點(diǎn) |
|
°C | ISO 306 | |
電氣性能 |
||||
| 介電強(qiáng)度 | thickness 3.2mm |
|
kV/mm | ASTM D149 |
| 高電弧燃燒指數(shù) |
|
無(wú) | UL 746A | |
| 表面電阻率 |
|
ohms | ASTM D257 | |
| 介電常數(shù) | frequency 50.0-60.0 hz |
|
無(wú) | ASTM D150 |
| 介電常數(shù) | frequency 1.00e+6 hz |
|
無(wú) | ASTM D150 |
| 相對(duì)漏電起痕指數(shù) |
|
V | UL 746A | |
| 耗散因數(shù) | frequency 50.0-60.0 hz |
|
無(wú) | ASTM D150 |
| 耗散因數(shù) | frequency 1.00e+6 hz |
|
無(wú) | ASTM D150 |
| 耐電弧性 |
|
sec | ASTM D495 | |
| 體積電阻率 |
|
ohms·cm | ASTM D257 | |
阻燃性能 |
||||
| 阻燃等級(jí) | thickness 1.47mm |
|
無(wú) | UL 94 |
其它性能 |
||||
| 熱絲引燃 (HWI) |
|
sec | UL 746A | |
| 相對(duì)溫度指數(shù) |
|
°C | UL 746B | |
| 相對(duì)溫度指數(shù) | 機(jī)械無(wú)沖擊 |
|
°C | UL 746B |
| 相對(duì)溫度指數(shù) | 機(jī)械沖擊 |
|
°C | UL 746B |